Effect of surface roughness on low-cycle fatigue behavior of type 304 stainless steel

Effect of surface roughness on low-cycle fatigue behavior of type 304 stainless steel

浏览量

The effects of surface roughness on the lowcycle fatigue life of Type 304 stainless steel at 593°C in air have been investigated. It is observed that, at a strain rate of 4 × 10 −3 s −1 and a total strain range of 1 pct, the fatigue life ( N f cycles) decreases with an increase in surface roughness. Information on crack growth vs strain cycles has been generated, as a function of surface roughness, by the measurement of striation spacing on fractured surfaces of specimens tested to failure. Crack propagation follows the In a ∞ N (where a is the crack length after N strain cycles) relation for longer specimen fatigue lives (N f > 2700 cycles) and departs from In a ∞ N for shorter fatigue lives. A quantitative estimate is made of the number of cycles N o ( r ) to generate a crack length